Fiber Contraction Approaches for Improving CMC Proportional Limit

The fact that the service life of ceramic matrix composites (CMC) decreases dramatically for stresses above the CMC proportional limit has triggered a variety of research activities to develop microstructural approaches that can significantly improve this limit. As discussed in a previous report, both local and global approaches exist for hindering the propagation of cracks through the CMC matrix, the physical source for the proportional limit. Local approaches include: (1) minimizing fiber diameter and matrix modulus; (2) maximizing fiber volume fraction, fiber modulus, and matrix toughness; and (3) optimizing fiber-matrix interfacial shear strength; all of which should reduce the stress concentration at the tip of cracks pre existing or created in the matrix during CMC service. Global approaches, as with pre-stressed concrete, center on seeking mechanisms for utilizing the reinforcing fiber to subject the matrix to in-situ compressive stresses which will remain stable during CMC service. Demonstrated CMC examples for the viability of this residual stress approach are based on strain mismatches between the fiber and matrix in their free states, such as, thermal expansion mismatch and creep mismatch. However, these particular mismatch approaches are application limited in that the residual stresses from expansion mismatch are optimum only at low CMC service temperatures and the residual stresses from creep mismatch are typically unidirectional and difficult to implement in complex-shaped CMC.