Dependence of Ru2O3 Activity on Composition of Silicate Melts: Using Statistical Correlations to Infer Thermodynamic Behavior in the Melt

Understanding variations in activity with composition is an essential step in improving prediction of partition coefficients during magma evolution. Variations in activity with composition are complex and do not generally exhibit ideal behavior relative to a traditional melt-component set. Although deviations from component ideality can be modeled numerically by simply fitting to compositional variables (such as in a regular or subregular solution model), such models have not been particularly successful for describing variations in trace component activities. A better approach might be to try to identify components that do a better job of describing the behavior of the species in the melt. Electrochemical Measurement of Ru2O3 activities: Electrodes were inserted into silicate melt beads of various compositions (Table 1) suspended on Ptwire loops in a 1-atm gas mixing furnace. An electrical potential was imposed between the electrodes, the imposed potential increasing along a step ramp with a pulse imposed on each step (Fig. 1). Current flows between electrodes when electroactive species in the melt are oxidized or reduced at the electrodes. The resulting current was measured at the top and bottom of the voltage pulse, and the difference (the differential current) was plotted against potential. The peak of the resulting curve is related to the activity coefficient for the particular electroactive species (Ru2O3) in the melt [1, 2, 3]. A significant part of the nonideal contribution to activity is due not to intrinsic properties of the component in the melt, but to our ignorance about the state and mixing properties of the component in the melt.