Commercialization of LARC (TradeMark) -SI Polyimide Technology

LARC(TradeMark)-SI, Langley Research Center- Soluble Imide, was developed in 1992, with the first patent issuing in 1997, and then subsequent patents issued in 1998 and 2000. Currently, this polymer has been successfully licensed by NASA, and has generated revenues, at the time of this reporting, in excess of $1.4 million. The success of this particular polymer has been due to many factors and many lessons learned to the point that the invention, while important, is the least significant part in the commercialization of this material. Commercial LARC(TradeMark)-SI is a polyimide composed of two molar equivalents of dianhydrides: 4,4 -oxydiphthalic anhydride (ODPA), and 3,3 ,4,4 -biphenyltetracarboxylic dianhydride (BPDA) and 3,4 -oxydianiline (3,4 -ODA) as the diamine. The unique feature of this aromatic polyimide is that it remains soluble after solution imidization in high-boiling, polar aprotic solvents, even at solids contents of 50-percent by weight. However, once isolated and heated above its T(sub g) of 240 C, it becomes insoluble and exhibits high-temperature thermoplastic melt-flow behavior. With these unique structure property characteristics, it was thought this would be an advantage to have an aromatic polyimide that is both solution and melt processable in the imide form. This could potentially lead to lower cost production as it was not as equipment- or labor-intensive as other high-performance polyimide materials that either precipitate or are intractable. This unique combination of properties allowed patents with broad claim coverage and potential commercialization. After the U.S. Patent applications were filed, a Small Business Innovation Research (SBIR) contract was awarded to Imtec, Inc. to develop and supply the polyimide to NASA and the general public. Some examples of demonstration parts made with LARC(TradeMark)-SI ranged from aircraft wire and multilayer printed-circuit boards, to gears, composite panels, supported adhesive tape, composite coatings, cookware, and polyimide foam. Even with its unique processing characteristics, the thermal and mechanical properties were not drastically different from other solution or meltprocessable polyimides developed by NASA. LARC(TradeMark)-SI risked becoming another interesting, but costly, high-performance material.