Static and dynamic fatigue behavior of glass filament-wound pressure vessels at ambient and cryogenic temperatures.

Investigation of the pressure load carrying capacity and fatigue strength of filament-wound glass-reinforced plastic pressure vessels subjected to static and cyclic loading at ambient and cryogenic (liquid nitrogen) temperature environments. The results indicate that the static fatigue problem is not critical at cryogenic temperatures. Under static loading at liquid nitrogen temperature, a reinforced plastic cylinder sustained pressurization for 88 days without failure at about 90% of the single cycle burst strength. At ambient temperature, the static life at 90% of the burst strength was about 7 min. Under cyclic loading in liquid nitrogen, no failure resulted after 1509 cycles at 55% of the single cycle burst strength. Under the same cyclic loading at ambient temperature, the test results would predict failure in the reinforced plastic. The results of similar tests upon adhesively bonded polyimide aluminum-foil lined cylinders are also reviewed.-