Ultrasonic and mechanical characterizations of fatigue states of graphite epoxy composite laminates

Results of an exploration of the relationship between ultrasonic attenuation and fatigue survivability of graphite fiber epoxy composites fabricated under different cure conditions are reported. A total of 9 27 x 40 cm eight-ply graphite epoxy laminated specimens were formed, and fatigue tests were run on five partial samples at 73.5 N varying at 30 Hz, with tests ending at a 1.27 cm deflection. A pulsed oscillator generated sinusoidal waves and transducers recorded the passage of the ultrasonic waves for display on oscilloscopes. Cure pressures ranged from 0.52-0.85 MPa and cure temperatures were in the 150-200 C interval. Ultrasonic through-transmission at 4 MHz was performed prior to and during fatigue testing. The minimum void volume fraction occurred at 175 C and 0.86 MPa. The flexural stiffness decreased with the number of fatigue cycles past 10,000, when the attenuation also increased. Correlations were found between the 4.0 MHz signal attenuation and the void volume fraction, and between the number of fatigue cycles to failure and the 4.0 MHz signal attenuation.