Measured thermal diffusivity of Hg(1-x)Cd(x)Te solids and melts

The thermal diffusivity of Hg(1-x)Cd(x)Te melts is found to rise rapidly with temperature to values characteristic of metals. Solid and melt diffusivities for values of x from 0 to 0.3 and over a temperature range from 150 to 900 C have been determined by the laser flash method of Parker, Taylor, and Cowan. The diffusivity decreases from a maximum at x = 0 in both the solid and the liquid, with the values observed at x = 0.3 being about 40 percent of those for x = 0. The solid diffusivity for x = 0 is 1.7 sq mm/s at 150 C, decreasing to 0.7 sq mm/s at the melting point. The x = 0 liquid diffusivity increases from 0.7 sq mm/s at the melting point to 3.5 sq mm/s at 900 C.