Sinterability, strength and oxidation of alpha silicon carbide powders

An investigation is made of pressureless sintering of commercially available alpha-SiC powders at temperatures between 1900 and 2150 C for periods of 10 to 240 min under one atmosphere of argon pressure. It is found that alpha-SiC powder containing boron and carbon sintering aids is sinterable at 2150 C for a period of 30 min to a high final density (greater than 96 percent of theoretical). In alpha-SiC powder containing aluminum and carbon sintering aids, the final density achieved is only about 80 percent of theoretical. Determinations are made of room temperature and high temperature (1370 C) flexure strength and oxidation resistance on sintered high density (more than 96 percent of theoretical) alpha-SiC (boron, carbon) material. It is found that both the strength and the resistance to oxidation are equivalent and comparable to those of the sintered alpha-SiC which represents the state of the art.