Fatigue behavior of continuous-fiber silicon carbide/aluminum compositesFour lay-ups of continuous fiber silicon carbide (SCS2) fiber/aluminum matrix composites were tested to assess fatigue mechanisms including stiffness loss when cycled below their respective fatigue limits. The lay-ups were 0 (sub 8), 0(sub 2)/ + or - 45 (sub 2s), 0/90 (sub 2s), and 0/ + or - 45/90 (subs). The data were compared with predictions from the author's previously published shakedown model which predicts fatigue-induced stiffness loss in metal matrix composites. A fifth lay-up, + or - 45 (sub 2s), was tested to compare shakedown and fatigue limits. The particular batch of silicon-carbide fibers tested in this program had a somewhat lower modulus (340 GPa) than expected and displayed poor bonding to the aluminum matrix. Good agreement was obtained between the stiffness loss model and the test data. The fatigue damage below the fatigue limit was primarily in the form of matrix cracking. The fatigue limit corresponded to the laminate shakedown for the + or - 45 (sub 2s) laminate.
Document ID
19860058279
Acquisition Source
Legacy CDMS
Document Type
Conference Paper
Authors
Johnson, W. S. (NASA Langley Research Center Hampton, VA, United States)
Wallis, R. R. (Foster-Miller Associates, Inc. Waltham, MA, United States)