Fatigue delamination behavior of PEEK thermoplastic composite laminatesThe delamination resistance of graphite-reinforced PEEK composites was quantified by conducting static and cyclic edge delamination tests on (35n/-35n/0n/90n)s AS4/PEEK laminates, where n = 1, 2. The experimentally determined mechanical delamination onset strains were used to calculate the critical strain-energy release rate for delamination onset as a function of fatigue cycle. The delamination onset strains decreased dramatically with fatigue cycles and then began to level off to an endurance limit at 1 million cycles. Although the static interlaminar fracture toughness of the AS4/PEEK composite is much greater than the toughness of graphite epoxy composites, the delamination fatigue threshold, calculated from the cyclic strain endurance limit at 1 million cycles, was only slightly greater than the threshold for graphite epoxy composites. The contribution of residual thermal stresses to delamination in the AS4/PEEK is substantial due to the large temperature range between the manufacture and the room temperatures.
Document ID
19870058750
Acquisition Source
Legacy CDMS
Document Type
Conference Paper
Authors
O'Brien, T. K. (NASA Langley Research Center; U.S. Army, Aerostructures Directorate, Hampton VA, United States)