Heterogeneous-nucleation and glass-formation studies of 56Ga2O3-44CaO

Glass formation and heterogeneous crystallization are described for the reluctant-glass-forming 56Ga2O3-44CaO eutectic composition. The times and temperatures for nucleation at various cooling rates and experimental conditions were measured and empirical continuous-cooling-crystallization boundaries were constructed for various heterogeneous nucleation processes. A definition for an empirical critical cooling rate to form a glass from reluctant borderline glass formers is proposed, i.e., the cooling rate that results in glass formation in 95 percent of the quenching experiments.