New ZrO2-Yb2O3 plasma-sprayed coatings for thermal barrier applications

New thermal barrier coatings, whose compositions were chosen on the basis of a limited study of the ZrO2-Yb2O3 system, were evaluated by cyclic testing in a furnace at 1120 C. On Ni-16.2Cr-5.9Al-0.15Y bond coating, ZrO2-12.4Yb2O3, ZrO2-14.7Yb2O3 and ZrO2-17.4Yb2O3 coatings have respectively 60, 30, and 15 percent longer lives than the near-optimum ZrO2-6.1Y2O3 coating. On Ni-18.3Cr-6.4Al-0.22Yb coating, ZrO2-12.4Yb2O3 has about 40 percent longer life than the ZrO2-6.1Y2O3 coating. The optimum Yb2O3 concentration in ZrO2 at which the maximum life is obtained is believed to be between 12.4 and 14.7 wt pct. The ZrO2-Yb2O3 thermal barrier systems failed through the formation of a crack or cracks in the thermal barrier coating near the bond coating interface. As-received ZrO2-Yb2O3 plasma spray powders had a nonhomogeneous distribution of Yb2O3. Monoclinic, cubic, and tetragonal phases in addition to Zr3Yb4O12 and an unknown phase were present.