Strength characterization of yttria/alumina-doped sintered silicon nitride

The flexural strength of yttria/alumina-doped sintered silicon nitride (Ford Material-RM 20) was measured as a function of temperature (20 to 1400 deg C), applied stress and time. Flexural stress rupture testing at 800 and 1000 deg C indicated that the material can sustain 344 MPa and 276 MPa, respectively, without failure, for a limited time (less than or equal to 100 h). The RM 20 material was susceptible to both oxidation and early stages of creep deformation at temperatures above 1000 deg C and displayed extensive creep deformation and degradation in strength above 1300 deg C.