Fundamentals of rapid solidification processing

An attempt is made to illustrate the continuous change that occurs in the solidification behavior of undercooled melts, as cooling rates increase from 0.0001 K/sec to about 1000 K/sec. At the higher cooling rates, more significant changes occur as the dendrite tip temperature begins to drop from the equilibrium liquidus. Discontinuous solidification behavior changes will occur if absolute stability is reached, or a metastable phase forms, or solidification proceeds to a glass rather than to a crystalline solid, or if there is significant undercooling prior to nucleation.