High Tc screen-printed YBa2Cu3O(7-x) films - Effect of the substrate material

Thick films of YBa2Cu3O(7-x) have been deposited on highly polished alumina, magnesia spinel, nickel aluminum titanate (Ni-Al-Ti), and barium tetratitanate (Ba-Ti) substrates by the screen printing technique. Properties of the films were found to be highly sensitive to the choice of the substrate material. The film on Ba-Ti turned green after firing, due to a reaction with the substrate and were insulating. A film on Ni-Al-Ti had a Tc (onset) of about 95 K and lost 90 percent of its resistance by about 75 K. However, even at 4 K it was not fully superconducting, possibly due to a reaction between the film and the substrate and interdiffusion of the reaction products. The film on alumina had Tc (onset) of about 96 K, Tc (zero) of about 66 K, and Delta Tc of about 10 K. The best film was obtained on spinel and had Tc (onset) of about 94 K, zero resistance at 81 K, and a transition width of about 7 K.