Laser action in chromium-activated forsterite for near infrared excitation

This paper reports on laser action in chromium-doped forsterite (Cr:Mg2SiO4) for 1064-nm excitation of the crystal's double-hump absorption band spanning the 850-1200-nm wavelength range. The cavity arrangement used for obtaining laser action in Cr:Mg2SiO2 was similar to that described by Petricevic et al. (1988). The fundamental and second harmonic emissions from a Q-switched Nd:YAG laser operating at a 10-Hz repetition rate were used for excitation of the NIR and visible bands, respectively. Pulsed laser action was readily observed for both the 1064-nm and 532-nm pumping at or above the respective thresholds. The laser parameters of the 532-nm and 1064-nm excitations were similar, indicating that the IR band is responsible for laser action for both excitations.