Effect of 0.1 at. pct Zirconium on the cyclic oxidation resistance of beta-NiAl

The effect of 0.1 at. pct Zr on the cyclic oxidation of hipped beta-NiAl was studied. Oxidation testing was performed in static air at 1100-1200 C, using 1-hr exposure cycles for test times up to 3000 hr. The weight change versus time data were modeled with the COSP computer program to analyze and predict cyclic-oxidation behavior. Zr additions significantly change the nature of the scale-spalling process during cooling, so that the oxide spalls near the oxide-air interface at a relatively low depth within the scale. Without Zr, the predominantly alpha-Al2O3 scale tends to spall randomly to bare metal at relatively high effective-scale-loss rates, particularly at 1150 C and 1200 C. This leads to higher rates of Al consumption for the Zr-free aluminide and much earlier depletion of Al, leading to eventual breakaway (i.e., failure).