The unusual near-threshold FCG behavior of a single crystal superalloy and the resolved shear stress as the crack driving force

An investigation of the fatigue growth (FCG) behavior of PWA 1480 single crystal nickel base superalloy was conducted. Typical Paris region behavior was observed above a Delta-K of 8 MPa sq rt m. However, below that stress intensity range, the alloy exhibted highly unusual behavior. The behavior consisted of a region where the crack growth rate became essentially independent of the applied stress intensity. The transition in the FCG behavior was related to a change in the observed crack growth mechanisms.