Tensile behaviour of blends of poly(vinylidene fluoride) with poly(methyl methacrylate)

Blends of poly(vinylidene fluoride) (PVF2) and poly(methyl methacrylate) (PMMA) were prepared over a wide concentration range and tested in tension at the same relative temperature below the glass transition. In nearly all blends, under conditions favoring disentanglement, (decrease in strain rate, or increase in test temperature), the yield stress and drawing stress decreased while the breaking strain increased. For materials with about the same degree of crystallinity, those with a higher proportion of amorphous PVF2 exhibited brittle-like behavior as a result of interlamellar tie molecules. In the semicrystalline blends, yield stress remains high as the test temperature approaches Tg, whereas in the amorphous blends the yield stress falls to zero near Tg. Results of physical aging support the role of interlamellar ties which cause semicrystalline blends to exhibit aging at temperatures above Tg.