The fatigue behaviour of orthotropic laminates under tension-compression loading

The fatigue behavior of orthotropic laminates (0, +/-45, 0 deg)2s and (90, +/-45, 90 deg)2s, has been evaluated under alternating tension-compression loading. Even though the first laminate is much stronger than the second, both started to fail by delamination. Visual damage started to show only at the very end of the fatigue life but measurement of the stiffness showed that degradation starts at about 80 percent of the fatigue life. The first laminate failed in compression after delamination between the 0 and the 45 deg laminae, while the second failed in tension after delamination between the +45 and -45 deg laminae. It is shown that the interlaminar fatigue strength of both laminate structures can be correlated to the applied fatigue load.