Fatigue damage in superalloys determined using Doppler broadening positron annihilation

Axial fatigue specimens of three superalloys, Inconel 718, Incoloy 903 and Haynes 188, were machined from solution-heat-treated material and artificially aged. They were subjected to cyclic loading for a selected number of cycles after which the S parameter was determined using Doppler broadening positron annihilation. Initially, the S parameter decreased, followed by a large increase and a subsequent decline leading to fracture. This has been interpreted as the removal of residual vacancies, the introduction of new defects by cyclic loading, and, finally, a clustering of the defects as microcracks which grow to cause failure.