Design Criteria for X-CRV Honeycomb Panels: A Preliminary Study

The objective of this project is to perform the first step in developing structural design criteria for composite sandwich panels that are to be used in the aeroshell of the crew return vehicle (X-CRV). The preliminary concept includes a simplified method for assessing the allowable strength in the laminate material. Ultimately, it is intended that the design criteria be extended to address the global response of the vehicle. This task will require execution of a test program as outlined in the recommendation section of this report. The aeroshell of the X-CRV is comprised of composite sandwich panels consisting of fiberite face sheets and a phenolic honeycomb core. The function of the crew return vehicle is to enable the safe return of injured or ill crewpersons from space station, the evacuation of crew in case of emergency or the return of crew if an orbiter is not available. A significant objective of the X-CRV project is to demonstrate that this vehicle can be designed, built and operated at lower cost and at a significantly faster development time. Development time can be reduced by driving out issues in both structural design and manufacturing concurrently. This means that structural design and analysis progresses in conjunction with manufacturing and testing. Preliminary tests results on laminate coupons are presented in the report. Based on these results a method for detection material failure in the material is presented. In the long term, extrapolation of coupon data to large scale structures may be inadequate. Test coupons used to develop failure criteria at the material scale are typically small when compared to the overall structure. Their inherent small size indicates that the material failure criteria can be used to predict localized failure of the structure, however, it can not be used to predict failure for all failure modes. Some failure modes occur only when the structure or one of its sub-components are studied as a whole. Conversely, localized failure may not indicate failure of the structure as a whole and the amount of reserve capacity, if any, should be assessed. To develop a complete design criteria experimental studies of the sandwich panel are needed. Only then can a conservative and accurate design criteria be developed. This criteria should include effects of flaws and defects, and environmental factors such as temperature and moisture. Preliminary results presented in this report suggest that a simplified analysis can be used to predict the strength of a laminate. Testing for environmental effects have yet to be included in this work. The so called 'rogue flaw test' appears to be a promising method for assessing the effect of a defect in a laminate. This method fits in quite well with the philosophy of achieving a damage tolerant design.