Lifetime Predictions of a Titanium Silicate Glass with Machined Flaws

A dynamic fatigue study was performed on a Titanium Silicate glass to assess its susceptibility to delayed failure and to compare the results with those of a previous study. Fracture mechanics techniques were used to analyze the results for the purpose of making lifetime predictions. The material strength and lifetime was seen to increase due to the removal of residual stress through grinding and polishing. Influence on time-to-failure is addressed for the case with and without residual stress present. Titanium silicate glass otherwise known as ultra-low expansion (ULE)* glass is a candidate for use in applications requiring low thermal expansion characteristics such as telescope mirrors. The Hubble Space Telescope s primary mirror was manufactured from ULE glass. ULE contains 7.5% titanium dioxide which in combination with silica results in a homogenous glass with a linear expansion coefficient near zero. delayed failure . This previous study was based on a 230/270 grit surface. The grinding and polishing process reduces the surface flaw size and subsurface damage, and relieves residual stress by removing the material with successively smaller grinding media. This results in an increase in strength of the optic during the grinding and polishing sequence. Thus, a second study was undertaken using samples with a surface finish typically achieved for mirror elements, to observe the effects of surface finishing on the time-to-failure predictions. An allowable stress can be calculated for this material based upon modulus of rupture data; however, this does not take into account the problem of delayed failure, most likely due to stress corrosion, which can significantly shorten lifetime. Fortunately, a theory based on fracture mechanics has been developed enabling lifetime predictions to be made for brittle materials susceptible to delayed failure. Knowledge of the factors governing the rate of subcritical flaw growth in a given environment enables the development of relations between lifetime, applied stress and failure probability for the material under study. Dynamic fatigue is one method of obtaining the necessary information to develop these relationships. In this study, the dynamic fatigue method was used to construct a time-to-failure diagram for polished ULE glass.