Mass transfer in a 1370 C (2500 F) lithium thermal convection loop

Experimental results from a test to evaluate interstitial element mass transfer effects on T-111, ASTAR 811C, and ASTAR 1211C after 5000 hours in flowing lithium at 1370 C (2500 F) are presented. No gross corrosion effects were observed. However, hafnium and nitrogen transfer to cooler regions within the loop were noted. Oxygen was in general removed from test specimens, but there was no evidence to indicate that it was a major factor in the mass transfer process. Carbon and hydrogen transfer were not detected.