Effect of long-time, elevated-temperature exposures to vacuum and lithium on the properties of a tantalum alloy, T-111

The effect of long-term, elevated-temperature vacuum and lithium exposures on the mechanical properties of T-111 (Ta-8W-2Hf) is determined. Exposure conditions were for 1000 hours at 980 or 1315 C, 5000 hours at 1315 C, and a duplex temperature exposure of 1000 hours at 980 C plus 4000 hours at 1040 C. The exposures resulted in reduced tensile and creep strengths of the T-111 in the 900 to 1100 C temperature range where a dynamic strain-age-strengthening mechanism is operative in this alloy. This strength reduction was attributed to the depletion of oxygen from solid solution in this alloy.