Directionally solidified lamellar eutectic superalloys by edge-defined, film-fed growth

A program was performed to scale up the edge-defined, film-fed growth (EFG) method for the gamma/gamma prime-beta eutectic alloy of the nominal composition Ni-19.7 Cb - 6 Cr-2.5 Al. Procedures and problem areas are described. Flat bars approximately 12 x 1.7 x 200 mm were grown, mostly at speeds of 38 mm/hr, and tensile tests on these bars at 25 and 1000 C showed lower strength than expected. The feasibility of growing hollow airfoils was also demonstrated by growing bars over 200 mm long with a teardrop shaped cross-section, having a major dimension of 12 mm and a maximum width of 5 mm.