Effect of minor reactive metal additions on fracture toughness of iron: 12-percent nickel alloy at-196 deg and 25 deg C

The slow bend precracked Charpy fracture toughness and tensile behavior of arc-melted and hot-rolled Fe-12Ni alloys containing up to 4 atomic percent reactive metal additions were determined at -196 C and 25 C after water quenching from three annealing temperatures. The fracture toughness of Fe-12Ni at -196 C was improved by small amounts of Al, Ce, Hf, La, Nb, Ta, Ti, V, Y, and Zr, but not by Si. Cryogenic toughness was improved up to 7.5 times that of binary Fe-12Ni and varied with the reactive metal, its concentration, and the annealing temperature.