Development of improved high pressure turbine outer gas path seal components

A plasma sprayed graded layered ceramic/metallic (ZrO2/CoCrAlY) seal was evaluated for JT9D turbine application by rig and engine tests. Four cyclic thermal shock rig tests were conducted during the program. Three completed 1000 simulated engine thermal cycle tests and the fourth completed 500 cycles without severe cracking or spalling. Three ceramic seals were installed in a JT9D experimental engine to evaluate the effect of the engine thermal environment on the seals. All three seals completed the test successfully without severe cracking or spalling. The three seals did have slight laminar cracks at the 85/15-40/60 ZrO2/CoCrAlY interface. The second engine test evaluated the rub capabilities of the seal. Six ceramic seals were installed in the engine with fourteen abrasive tip blades. Three of the six seals rubbed to a depth of 24 mils. Eight of the fourteen abrasive tip blades showed evidence of wear. Three of the eight blades wore a maximum of five mils. Engine rub test results demonstrated the potential of reducing turbine clearances and thereby improving engine performance by use of sprayed ceramic seals.