Investigation of the reaction kinetics between SiC fibers and selectively alloyed titanium matrix composites and determination of their mechanical properties

During high temperature exposure, an interfacial reaction occurs between SiC fiber reinforcement and titanium matrices which can be detrimental to the mechanical properties of the composite. The reaction kinetics between SCS-6 fibers and Ti-1100 were determined at 800 to 1000 C and found to be slower than those of other currently used titanium alloys (Ti-15-3, Ti-6-4). The experimentally determined reaction kinetics for Ti-1100 were extrapolated to 700 C and found to accurately predict reaction zone size after 1000 hours of exposure. Predictions of the time to consume the surface layer on the SCS-6 and SCS-9 fibers were made in an effort to estimate the time that the fiber will retain its strength in Ti-1100 during isothermal exposure at high temperatures. Using this approach, the strength of an SCS-6 fiber in Ti-1100 should be retained for over 20,000 hours at isothermal exposures less than 800 C. Strength predictions using the rule of mixtures for a unidirectional Ti-1100/SCS-6 composite are presented for short term exposures up to 700 C. Room temperature tests of an as-fabricated 20 volume percent fiber/Ti-1100 composite yielded a UTS of 226 ksi (1490 MPa) which is close to that predicted by the ROM.