Measurement of a surface heat flux and temperature

The Heat Flux Microsensor is a new sensor which was recently patented by Virginia Tech and is just starting to be marketed by Vatell Corp. The sensor is made using the thin-film microfabrication techniques directly on the material that is to be measured. It consists of several thin-film layers forming a differential thermopile across a thermal resistance layer. The measured heat flux q is proportional to the temperature difference across the resistance layer q= k(sub g)/delta(sub g) x (t(sub 1) - T(sub 2)), where k(sub g) is the thermal conductivity and delta (sub g) is the thickness of the thermal resistance layer. Because the gages are sputter coated directly onto the surface, their total thickness is less than 2 micrometers, which is two orders of magnitude thinner than previous gages. The resulting temperature difference across the thermal resistance layer (delta is less than 1 micrometer) is very small even at high heat fluxes. To generate a measurable signal many thermocouple pairs are put in series to form a differential thermopile. The combination of series thermocouple junctions and thin-film design creates a gage with very attractive characteristics. It is not only physically non-intrusive to the flow, but also causes minimal disruption of the surface temperature. Because it is so thin, the response time is less than 20 microsec. Consequently, the frequency response is flat from 0 to over 50 kHz. Moreover, the signal of the Heat Flux Microsensor is directly proportional to the heat flux. Therefore, it can easily be used in both steady and transient flows, and it measures both the steady and unsteady components of the surface heat flux. A version of the Heat Flux Microsensor has been developed to meet the harsh demands of combustion environments. These gages use platinum and platinum-10 percent rhodium as the thermoelectric materials. The thermal resistance layer is silicon monoxide and a protective coating of Al2O3 is deposited on top of the sensor. The superimposed thin-film pattern of all six layers is presented. The large pads are for connection with pins used to bring the signal out the back of the ceramic. In addition to the heat flux measurement, the surface temperature is measured with a platinum resistance layer (RTS). The resistance of this layer increases with increasing temperature. Therefore, these gages simultaneously measure the surface temperature and heat flux. The demonstrated applications include rocket nozzles, SCRAM jet engines, gas turbine engines, boiling heat transfer, flame experiments, basic fluid heat transfer, hypersonic flight, and shock tube testing. The laboratory involves using one of these sensors in a small combustion flame. The sensor is made on a 2.5 cm diameter piece of aluminum nitride ceramic.