Processing and Properties of Fiber Reinforced Polymeric Matrix Composites: Processing Robustness of IM7/PETI Polyimide Composites - Part 2

The processability of a phenylethynyl terminated imide (PETI) resin matrix composite was investigated. Unidirectional prepregs were made by coating an N-methylpyrrolidone solution of the amide acid oligomer onto unsized IM7. Two batches of prepregs were used: one was made by NASA in-house, and the other was from an industrial source. The composite processing robustness was investigated with respect to the effect of B-staging conditions, the prepreg shelf life, and the optimal processing window. Rheological measurements indicated that PETI's processability was only slightly affected over a wide range of B-staging temperatures (from 250 C to 300 C). The open hole compression (OHC) strength values were statistically indistinguishable among specimens consolidated using various B-staging conditions. Prepreg rheology and OHC strengths were also found not to be affected by prolonged (i.e., up to 60 days) ambient storage. An optimal processing window was established using response surface methodology. It was found that IM7/PETI composite is more sensitive to the consolidation temperature than to the consolidation pressure. A good consolidation was achievable at 371 C/100 Psi, which yielded an OHC strength of 62 Ksi at room temperature. However, processability declined dramatically at temperatures below 350 C.