Study of a columnar grain structure produced in a superalloy by gradient-annealing prealloyed powder extrusions

Annealing in a temperature gradient was used to produce a structure of continuous columnar grains in alloy 713 C made by extrusion of prealloyed powder. The columnar-grained specimens had tensile strengths within plus or minus 5 percent of those of the as-cast alloy at 760 C and 980 C but were significantly stronger at room temperature. Stress-rupture tests at 760 C and 980 C showed lives scattered from 17 to 376 percent of those of as-cast 713 C tested under the same conditions. X-ray diffraction studies showed the large grains formed upon annealing to have a well-defined texture, although the as-extruded material had none.