Development of thermally stable phosphonitrile elastomers for advanced aerospace structures

Attempts to prepare low molecular weight, curable poly-(fluoroalkoxyphosphazenes) have been successful. Derivatization of /Cl2PN/n polymer with alkoxides gave functionally reactive terpolymers. These terpolymers could be crosslinked with polyisocyanates at room temperature. Attempts to control molecular weight have not been as successful. The effects of (Cl2PN)3 monomer purity, use of (Cl2PN)3,4 mixture, and early termination of the bulk polymerization of (Cl2PN)3 were studied briefly. Both low and high molecular weight polymers were obtained. Reaction of NH4Cl with PCl5 with subsequent heating to give chain extension gave either gels of oils with molecular weights of several thousand. The stabilization of poly-(fluoroalkoxyphosphazene) was investigated. The results generally were inconclusive, but acids were found to be deleterious while bases had little discernible effect. Improvements in stability by modification of end groups was inconclusive.