Effect of autoclave heat treatments on the mechanical properties of the prealloyed powder cobalt-base alloy HS-31

The cobalt-base alloy HS-31 was atomized into powder and then consolidated by extrusion or by hot isostatic pressing (HIP) in an autoclave over a range of temperatures spanning the solidus, approximately 2340 F. Extrusions were subsequently autoclaved at the same conditions. Extrusions autoclaved at 2420 F had a life of 300 hours at 1200 F and 30 hours at 1800 F at stresses that result in a 10-hour life with cast HS-31. Superior stress rupture lives of autoclaved material are probably related to the solidification structure at the grain boundaries as well as to the increased grain size.