The effect of oxygen concentration on the boundary lubricating characteristics of an unformulated C-ether to 300 C

The effect of oxygen concentration on the boundary lubricating characteristics of an unformulated C-ether was studied with the use of a ball-on disk sliding-friction apparatus. Results were compared with those obtained with a polyphenyl ether. Experimental conditions included oxygen concentrations ranging from 20 percent (air) to 0.001 percent (nitrogen), a load of 1 kilogram, a sliding speed of 17 meters per minute, and disk temperatures ranging from 20 to 300 C (77 to 572 F). The C-ether yielded better boundary lubricating characteristics than did the polyphenyl ether in air and nitrogen over most of the temperature range. The C-ether exhibited lower wear at high oxygen levels (10 to 20 percent O2) from 25 to 200 C (77 to 392 F) and at low oxygen levels (0.001 to 1.0 percent O2) from 200 to 300 C (392 to 572 F). Friction polymer was observed around the wear scars of most test specimens. Friction polymer generation and its effect on wear are discussed in light of current theories.