Ultraviolet and charged particle irradiation of proposed solar cell coverslide materials and conductive coatings for the Helios spacecraft

Coverslide materials consisting of Corning 7940 fused silica, multilayers of titanium and manganese oxides (blue reflector), and indium oxide (conductive-coating) were exposed to 16 UVSC up to 800 EUVSH in vacuum. Slight changes in optical transmittance and optical absorptance were found in the (200-360) millimicron regions of the fused silica and conductive coating respectively. Exposure to 4 KeV protons and 4.5 KeV electrons in vacuum, produced decreases of several percent in transmittance, (200-360) millimicron region in the fused silicas after total fluxes less or = 10 to the 14th power particles/sq cm. Sheet resistance of the conductive coating increased above 1.0 kilo-ohm/square after a total flux less or = 10 to the 14th power particles/sq cm. Solar cells with coverglasses utilizing the indium oxide conductive coating were exposed to 1 Mev electrons and 1 Mev protons in air and in vacuum. Total fluxes ranged from 10 to the 11th power particles/sq cm to 10 to the 15th power particle/sq cm. There was no appreciable degradation in the resistance of the conductive coating during or after these tests.