Reliable nondestructive inspection for incomplete weldment penetration and rapid oxidation of aluminum surfaces when exposed to the atmosphere are currently two major problems in welded aluminum spacecraft structure. Incomplete-penetration defects are extremely difficult to detect and can lead to catastrophic failure of the structure. The moisture absorbed by aluminum oxide on the surface can cause weldment porosity if the surface is not cleaned before welding. The approach employed in this program to solve both problems was to employ copper as a coating to prevent oxidation of the aluminum. Also, copper was used as an opaque additive in the weldment to enhance X-ray detection in the event of incomplete penetration.