Development of large diameter carbon monofilament

A process for preparing large diameter carbon-boron monofilament was developed. The process involves chemical vapor depositing a carbon-boron alloy monofilament from a BCl3, CH4, and H2 gas mixture onto a carbon substrate. Amorphous alloys were formed when gaseous mixtures containing greater than 20 percent methane (80 percent BCl3) were used. The longest uninterrupted lengths of carbon-boron monofilament were produced using a CH4/BCl3 gas ratio of 2.34. It was found that the properties of the carbon-boron alloy monofilament improved when the carbon substrate was precleaned in chlorine. The highest strength monofilament was attained when a CH4/BCl3 gas volume ratio of 0.44 was 28 million N/sq cm (40 million psi). While the highest strengths were attained in this run, the 0.44 gas ratio and other CH4/BCl3 ratios less than 2.34 would not yield long runs. Runs using these ratios were usually terminated because of a break in the monofilament within the reactor. It is felt better process control could probably be achieved by varying the amount of hydrogen; the BCl3/H2 ratio was kept constant in these studies.