Improvement program for polycarbonate capacitors

Hermetically sealed, wound, AC, polycarbonate capacitors incorporating design improvements recommended in a previous study were designed and built. A 5000 hour, 400 Hz ac life test was conducted using 384 of these capacitors to verify the adequacy of the design improvements. The improvements incorporated in the capacitors designed for this program eliminated the major cause of failure found in the preceding work, termination failure. A failure cause not present in the previous test became significant in this test with capacitors built from one lot of polycarbonate film. The samples from this lot accounted for 25 percent of the total test complement. Analyses of failed samples showed that the film had an excessive solvent content. This solvent problem was found in 37 of the total 46 failures which occurred in this test. The other nine were random failures resulting from causes such as seal leaks, foreign particles, and possibly wrinkles.