Filament winding S-glass/polyimide resin composite processing studies

The work performed in selecting a TRW A-type polyimide resin that would be suitable for fabrication of filament wound reinforced plastic structures is described. Several different formulations were evaluated after which the P105AC formulation was selected as the most promising. Procedures then were developed for preparing P105AC/S-glass roving prepreg and for fabricating filament wound structural composites. Composites were fabricated and then tested in order to obtain tensile and shear strength information. Small, closed-end cylindrical pressure vessels then were fabricated using a stainless steel liner and end fittings with a P105AC/S-glass polar wound overwrap. These pressure vessels were cured in an air circulating oven without augmented pressure. It is concluded that the P105AC resin system is suitable for filament winding; that low void content, high strength composites are obtained by the filament winding process; and that augmented pressure is not required to effect the fabrication of filament wound P105AC composites.