Directionally solidified composite systems under evaluation

The directionally solidified eutectic in-situ composites being evaluated for use as turbine materials range from ductile-ductile systems, where both matrix and reinforcement are ductile, to brittle-brittle systems, where both phases are brittle. The alloys most likely to be used in gas turbine engines in the near term are the lamellar ductile-semi ductile alloys gamma prime-delta, Ni3Al-Ni3Nb and gamma/gamma prime-delta Ni,Cr,Cb,Al/Ni3Al-Ni3Nb and the fibrous ductile-brittle alloys M-MC CoTaC or NiTaC and M-M7C3(Co,Cr,Al)-(Cr,Co)7C3. The results of tests are given which indicate that gamma prime strengthened NiTaC alloys and a (Co,Cr,Al)7C3 have greater tensile strength than the strongest superalloys at temperatures up to about 600 C. The gamma prime-delta and gamma/gamma prime-delta alloys in the Ni,Al,Nb(Cr) systems have greater tensile strength than the superalloys at temperatures greater than 800 C. At low stresses fibrous carbide reinforced eutectic alloys have longer lives at high temperatures than the strongest superalloys. Lamellar delta, Ni3Nb reinforced eutectic alloys have longer lives at high temperatures than the strongest superalloys at all stresses. The experience currently being gained in designing with the brittle ceramics SiC and Si3N4 may eventually be applied to ceramic matrix eutectic in-situ composites. However, the refractory metal fiber reinforced brittle-ductile systems may find acceptance as turbine materials before the ceramic-ceramic brittle-brittle systems.