Compositional effects on mechanical properties of hafnium-carbide-strengthened molybdenum alloys

The mechanical properties of swaged rod thermomechanically processed from arc melted Mo-2Re-Hf-C alloys containing as much as 0.9-mol% HfC were evaluated. The low-temperature ductilities of these alloys were not influenced by the amount of HfC present but by the amount of Hf in excess of stoichiometry. Maximum ductility occurred at 0.2- to 0.3-at.% excess Hf. At 0.3- to 0.5-mol% HfC, alloy strength varied directly with the Mo content of extracted carbide particles, both decreasing as the amount of excess Hf increased. Additions of 2-at.% Re had little effect on strength or ductility. Tensile and creep strengths of Mo-2Re-0.7Hf-0.5C alloy equaled or exceeded those of other high strength Mo alloys.