Deformation characteristics and time-dependent notch sensitivity of Udimet 700 at intermediate temperatures

Time-dependent notch sensitivity of Udimet 700 sheet, bar, and investment castings was observed between 1000 and 1400 F (538-760 C) but not at 1600 F (871 C). As was the case for Modified Waspaloy, Waspaloy, Rene 41, Inconel 718, and TD-NiCr, it occurred when notched specimens were loaded below the yield strength and when creep deformation was localized. For each gamma-prime strengthened alloy and notched specimen geometry, a stress-average particle size zone can be defined to characterize the notch-sensitive behavior.