Feasibility investigation of growing gallium arsenide single crystals in ribbon form

Polycrystalline GaAs ribbons have been grown in graphite boats by passage of a wide zone through B2O3 encapsulated feed stock, confined by a quartz cover plate. By controlling the heat flow in the graphite boat and controlling the zoning rate, large grained, single phase polycrystalline samples with directional solidification and good thickness control were achieved. Arsenic vaporization was effectively suppressed at the melting point of GaAs by the B2O3 moat and 3 atmospheres of pressure. A vertical constrained-zone-melting apparatus with a B2O3 moat seal, rf heating, and water cooling on the bottom will be used to control the heat flow and temperature patterns required for growth of single crystal ribbons.