An evaluation of dry film lubricants and substrate materials for use on SSME gimbal bearings

Failure of the spherical bearing shaft of the Space Shuttle Main Engine (SSME) gimbal bearing assembly was encountered during Design Verification Specification testing of the full scale engine. Investigation revealed that the failure was caused by a deficiency in the lubrication system. Based upon the materials and gimbal operating conditions, a lubricant of MoS2 and graphite with a ceramic binder was the best lubricant candidate for this particular application; however, the decision to implement the change was not made without verification testing. Scaled down simulation testing was performed. Four different substrate materials and eight different dry film lubricants were subjected to tests under simulated SSME environmental and stress load conditions. The test specimens were evaluated for friction and operating life. Each test specimen was subjected to cyclic operation under load until failure. The force required to move the bearing surfaces relative to each other was monitored throughout the test, thus providing analytical data for derivation of the coefficient of friction. Results indicate that the MoS2/graphite lubricant with ceramic binder proved to be superior from the standpoint of endurance and also from the standpoint of friction reducing capabilities when applied to the titanium substrate material used on SSME. Endurance of this lubricant was approximately 16 times that of the lubricant which was being used when the SSME gimbal failed.