Space processing of chalcogenide glass

The manner in which the weightless, containerless nature of in-space processing can be successfully utilized to improve the quality of infrared transmitting chalcogenide glasses was investigated. The following conclusions were reached: (1) Laboratory experiments have established the techniques, processes and equipment necessary for the production of high purity chalcogenide glasses. (2) Processing techniques have been successfully adopted for Ge28Sb12Se60 glass in a 1-g environment. (3) The Ge28Sb12Se60 glasses that have been processed have optical transmission around 63% (5 mm thick). (4) Laboratory experiments have established that the use of precursor materials in powdered form increases the oxygen contamination of the processed glass. This indicates that high purity precursor materials in bar or pellet form should be used. (5) Modifications were made on the MSFC acoustic levitator in an attempt to improve levitation stability during long-time experiments. Room temperature experiments on As2S3 glasses and high temperature experiments on polystyrene were conducted.