Optimized Selective Coatings for Solar Collectors

The spectral reflectance properties of black nickel electroplated over stainless steel and of black copper produced by oxidation of copper sheet were measured for various plating times of black nickel and for various lengths of time of oxidation of the copper sheet, and compared to black chrome over nickel and to converted zinc. It was determined that there was an optimum time for both plating of black nickel and for the oxidation of copper black. At this time the solar selective properties show high absorptance in the solar spectrum and low emittance in the infrared. The conditions are compared for production of optimum optical properties for black nickel, black copper, black chrome, and two black zinc conversions which at the same conditions had absorptances of 0.84, 0.90, 0.95, 0.84, and 0.92, respectively, and emittances of 0.18, 0.08, 0.09, 0.10, and 0.08, respectively.