Estimating surface temperature in forced convection nucleate boiling: A simplified method

During a test program to investigate low-cycle thermal fatigue, 21 of 22 cylindrical test sections of a cylindrical rocket thrust chamber were thermally cycled to failure. Cylinder liners were fabricated from OFHC copper, Amzirc, and NARloy-Z. The cylinders were fabricated by milling cooling channels into the liner and closing out the backside with electrodeposited copper. The tests were conducted at a chamber pressure of 4.14 MN/sq m (600 psia) and an oxidant-fuel ratio of 6.0 using hydrogen-oxygen as propellants. The average throat heat flux was 54 MW/sq m (33 Btu/sq in./sec). All of the failures were characterized by a thinning of the cooling channel wall and eventual failure by tensile rupture. The 1/2-hard Amzirc material showed little improvement in cyclic life when compared with OFHC copper; while the NARloy-Z and aged Amzirc materials had the best cyclic life characteristics. One OFHC copper cylinder was thermall cycled 2044 times at a steady-state hot-gas-side wall temperature of 514 K (925 R) without failing.