Electrochemical behavior of 0.2 to 3 molar ferrous chloride-ferric chloride mixtures on edge-on pyrolytic graphite rotated disk electrodes

Potentiostatic determinations in various mixtures of FeCl2-FeCl3 with excess HCl show rest potentials that are 0.1 V less electropositive than the theoretical values from the formulated ratios of FeII to FeIII (probably as a result of complexing). The standard rate constant sub s. ranges between 0.0001 and 0.000 cm/sec. Tafel slopes b of roughly 0.12V per decade indicate single-electron exchange kinetics. No significant trend in either b or sub s was attributed to mixture composition. The higher sub s. values occurred with and edge-on pyrolytic graphite that had undergone a permanent surface change.