Kinetics of imidization and crosslinking in PMR-polyimide resin

Infrared spectroscopy and differential scanning calorimetry were employed to study the imidization and crosslinking kinetics of norbornenyl-capped, addition-type polyimide resins (designated PMR for polymerization of monomer reactants). The spectral and thermal analyses were performed on resin specimens which had been isothermally aged at temperatures appropriate for imidization (120 to 204 C) and crosslinking (275 to 325 C). Imidization occurs rapidly (approximately 0.01/min) at short times, while at times longer than approximately 0.5 hour, the rate decreases significantly (approximately 0.0001/min). The crosslinking reaction exhibits first order kinetics during the initial portion of the reaction and its rate appears to be limited by the reversion of the norbornenyl Diels-Alder adduct. The total heat evolved per mole of endcap during crosslinking shows an inverse dependence on the molecular weight of the imide prepolymers. This reflects the effect of endcap dilution and decreased mobility of the larger oligomers.