The effect of oxidation-expanded defects upon MOS parameters

Implantation of Ne ions was chosen as a means of introducing a uniformly distributed quantitatively controllable and reproducible amount of microdefects at the silicon surface. Each wafer was ion-implanted on one half of its surface, the other half remaining as a control. Seven implant fluences from 1 trillion to 5 by 10 to the 14th power Ne ions/sq cm were used. The fluences, as well as the concentrations of defects expanded by the subsequent gate oxidation, were correlated with seven different MOS parameters. For implant fluences of 10 to the 14th power per sq cm and above, increasing stacking-fault densities were found. The oxide defect density associated with time-dependent breakdown increased significantly with Ne dose. The presence of oxidation-expanded defects drastically increases the surface-generation velocity and decreases the bulk lifetime. Slight increases in flatband voltage and surface-state density occurred only for the wafers having the greatest defect concentrations. Oxidation of a P-containing damaged silicon surface results in a greater pileup of P at the surface than occurs for the oxidation of a similar but undamaged surface. It appears that the expanding defects restrain the diffusion of P inward from the surface.